UT White Dental Zirconia Block

Sintering Temperature	1450 °C
3-Point Bending Strength	≥ 600 MPa
Translucency	~ 48%
Vickers Hardness (Hv10)	> 1200
Typical indication	Full Zirconia, Anterior Veneer, Inlay, Crown, Bridge
Coloring Liquid	Not available
Pre-shaded Blank	White
Applicative Systems	Open System, Amann Girrbach System, ZirKon Zahn System
Available Thickness	10 mm, 12 mm, 14 mm, 16 mm, 18 mm, 20 mm, 22 mm, 25 mm, Customization

【Physical and Chemical properties】

Sintered density: ≥ 6.02 g/cm3

Sintered bending strength : check table above

Translucency:check table above

Optimize Max temperature: 1450℃.

Holding 120min at Max temperature

Do not open the furnace door above 80℃ to avoid thermal shock stress

Recommend sintering progam as following: